| Customization: | Available |
|---|---|
| Material: | Polyurethanes/PU |
| Usage: | Engineering Plastics |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
SDP1133 cold storage insulation system blend polyol is a kind of spray rigid PU foam blend polyol, specially used for the insulation of the wall of storage insulation. It used together with isocyanate(PM-200) to make rigid PU foam through PU spray machine. The foam produced has the characteristics as following:
The strong adhesive force, convenient construction and no seams.
The low thermal conductivity, low water absorption and good dimensional stability. The long service life.
| Physical Properities Test Method Standard Metric Value | ||||
| Core Density | GB/T 6343-2009 | kg/m3 | 38.3 | |
| Compressive Strength | GB/T 8813-2008 | kPa | 264 | |
| Tensile Strength | GB/T 9641-88 | kPa | 136 | |
| Oxygen index | GB/T 2406.2-2009 | % | 23.4 | |
| Initial Thermal Conductivity | GB/T 10294-2008 | W/(m·K) | 0.023 | |
| Close Cell Content | GB/T 10799-2008 | % | ≥88 | |
| Water Absorption | GB/T 8810-2005 | % | ≤3 | |
| Dimensional Stability (Foam made After 6 days) |
-25ºC 70ºC |
GB/T 8811-2008 | % | ≤±1 |
| ≤±1 | ||||
| Property Blend polyol Polymeric MDI | ||
| Product Name | SDP1133 | PM200 |
| Appearance | Light yellow liquid | Brown liquid |
| Density( 25°C) | 1.10±0.10 g/cm3 | 1.22-1.25 g/cm3 |
| Viscosity( 25°C) | 300±100 cps | 200±50 cps |
| Shelf Life | 6 months | 12 months |
SDP1133:PM200=1:1 (Volume Ratio)
Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.
The thickness of one gun spray foam should not exceed 50 mm. If over 50mm, which may cause foam charring or spontaneous combustion and poor foam performance.
It is suggested that spray next layer of the foam after the internal temperature of last spray foam blow 25ºC. And the maximum thickness spray during 24h period is 203mm(8inches).
Like most of foam product, foam made by SDP1133 is combustible. An thermal barrier must be installed in accordance with approved construction standards.
The service temperature of the foam with SDP1133 is between -60~80ºC.
220KGS/drum, blue paint or zinc coating drums (Drum Weight: 18-23kgs)
The blend polyol should be stored in the sealed container to avoid the absorption of water vapor. During the transportation, it should avoid serious shake and strong sunlight. It should be stored in ventilated place, avoiding light, water and fire. Recommended storage temperature is 15~25ºC.
Direct contact with SDP1133 type blend polyol can lead to moderate eye irritation and mild skin irritation, which can cause skin allergies. Repeated inhalation of high concentration of volatile gas will cause respiratory allergy, and should be treated immediately. Anti- inflammatory and anti-allergic treatment measures should be taken.
Please be careful in the operation to prevent contact with the skin and splash into the eye, please wear the necessary protective equipment (gloves, protective goggles, working clothes, etc.).
Once splashed on the skin or the eye, rinse with water immediately for at least 15 minutes, and the skin is washed with soapy water. Please seek medical treatment immediately after swallowed.
){kind=link}