The performance of high wear-resistant polyurea coating meets the national standard GB/T 23446-2009 Type II index, and is applied using specialized spraying equipment in China.The coating instantly solidifies, forming a high-strength, high elongation, and seamless elastic waterproof coating film.
Product Features
100% solid content, environmentally friendly new materials;
Rapid curing, reaching walking strength in 10 minutes, continuous spraying on the facade and top surface without sagging;
Low sensitivity to temperature and humidity reduces the risk of foaming in polyurethane waterproof coatings;
Spray continuously without seams, eliminating the risk of leakage;
The coating is dense, continuous, highly elastic, and has excellent waterproof performance;
High strength, high elongation, high tear strength, able to withstand erosion by water, seawater, acid, alkali, salt, etc;
Excellent crack tracking ability, able to withstand structural deformation without damage to the polyurea coating itself.
Product Parameters
Solids:≥98%
Density (mixed, 25 ºC): 1.15 ± 0.05g/cm3
Volume mixing ratio A: R=1:1
Construction Conditions
The temperature of the environment and grassroots is between -10 ºC and 30 ºC;
Air humidity ≤ 85%;
Substrate temperature: must be at least 3 ºC higher than the air dew point temperature;
Airless spraying.
Product Parameters
Performance
| Project |
Index |
| Solid content,% |
≥98 |
| Gel time, s |
≤45 |
| Dry time, s |
≤120 |
| Tensile strength, MPa |
≥16 |
| Elongation at break,% |
≥450 |
| Tear strength, N/mm |
≥50 |
| Low temperature bending resistance, ºC |
≤-40 |
| Impermeability |
0.4MPa, 2-hour impermeable |
| Heating expansion and contraction rate,% |
≤1.0 |
| Bond strength, MPa |
≥2.5 |
| Water absorption rate,% |
≤5.0 |
| Aging during fixed extension |
heat aging |
No cracks or deformations |
| artificial weathering |
No cracks or deformations |
| Heat treatment |
Tensile strength retention rate,% |
80-150 |
| Elongation at break,% |
≥400 |
| Low temperature bending resistance, ºC |
≤-35 |
| Alkaline treatment |
Tensile strength retention rate,% |
80-150 |
| Elongation at break,% |
≥400 |
| Low temperature bending resistance, ºC |
≤-35 |
| Acidation |
Tensile strength retention rate,% |
80-150 |
| Elongation at break,% |
≥400 |
| Low temperature bending resistance, ºC |
≤-35 |
| Salting |
Tensile strength retention rate,% |
80-150
|
| Elongation at break,% |
≥400 |
| Low temperature bending resistance, ºC |
≤-35 |
| Hardness (Shore A) |
≥80 |
| Wear resistance (750g, 500r)/mg |
≤30 |
| Impact resistance/kg · m |
≥1.0 |
Packaging & Shipping
Packaging
Certifications
Certifications
Company Profile
Company Profile
Shunda Company founded in year 1996, is a leading manufacturer of rigid PU foam blend polyol System material, our annual sales reached 50,000 MT in the past three years. We have four Manufacturer plants in Yantai, Linyi, Dalian and Chang chun with totally more than 400 employees by now. For over 20 years development, Yantai Shunda Polyurethane Co., Ltd has grown up into a modern joint-stock enterprise, which has the research, development, production and operation for the series of rigid polyurethane foam production. We are also the largest global distributor of MDI series of Wanhua Chemical. Depending on our own strong R&D capability,professional purchasing team, quality control ability and full MDI series product supply, we could supply all series of PU raw material to the internal and abroad customers and undertake the engineering of the insulation project.
Yantai Sanjing Chemical Industry Materials Co., Ltd is established in 2010 by Shunda Group as its International sale company, its mainly engaged in Blend polyol, Polyetherpolyol, flameretardants, PU catalysts, Polymeric MDI and other raw materials which are widely used for the insulation of wall and roof building, coldstorage, ship, sandwichpanel, refrigerators, freezers, pipelines, garage door and etc.
Audited Supplier 
){kind=link}