Best Price Blend Polyol PU Foam Raw Material for Pipe Line Insulation

• Customization: Available
• Material: Polyurethanes/PU
• Usage: Engineering Plastics
• Model NO.: SDB10F
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Blow Molding
• Color: White
• Cream Time: 15-20s
• Gel Time: 100-120s
• Rise Time: 160-200
• Physical Properities: 35~46kg/M3
• Compressive Strength: 200~300kpa
• Transport Package: Iron Drum
• Specification: 250kg
• Trademark: SHUNDA
• Origin: China
• HS Code: 39072090
• Production Capacity: 50000ton/Year
• Package Size: 60.00cm * 60.00cm * 90.00cm
• Package Gross Weight: 17.000kg

Product Description

High Quality Blend Polyol Rigid PU Foam for Pipe Injection Insulation
SDB10F is a kind of blend polyol of whole water system used in pipe insulation. This kind of product use zero ozone depleting blowing agent (0 ODP), SDB10F use CO2 as the blowing agent, which produced through the reaction of water and isocyanate. Every performance of SDB10F finished foam products can meet the requirements of GB/T29047 standard.
The foam produced has the characteristics as following:

1. Water blowing agent, environmental protection, zero ozone depleting blowing agent(0 ODP).
2. Every performance of the foam product meets the requirements of GB/T29047 standard.
3. Every performance of the foam product is very stable.

Product Parameters

TYPICAL PHYSICAL PROPERTIES

Physical Properities	Test Method	Metric	Value
Core Density	GB/T 6343-2009	kg/m^3	≥60
Radial Compressive Strength	GB/T 8813-2008	MPa	≥0.3
Initial Thermal Conductivity(50°C)	GB/T 10294-2008	W/(m·K)	≤0.033
Close Cell Content	GB/T 10799-2008	%	≥88
Water Absorption	GB/T 8810-2005	%	≤10
Air bubbles	GB/T 29047	mm	1/3Insulation Thickness.
Average cell size.	GB/T 29047	mm	≤0.5

Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.