Blend Polyol for Rigid PU Foam for Pipe Injection Insulation

• Material: Polyurethanes/PU
• Usage: Engineering Plastics
• Plastic Properties After Heated: Thermosetting Plastic
• Plastic Forming Method: Injection
• Color: Yellow
• Transport Package: Iron Drum
• Model NO.: SDB10D-Z02
• Specification: 200kg
• Trademark: shunda
• Origin: China
• HS Code: 39072090
• Production Capacity: 100000tons

Product Description

DESCRIPTION
SDB10D-Z02 is a kind of blend polyol used for pipe insulation system for city heating or cooling. When it combined with isocyanate(PM200) leads to the formation of rigid polyurethane foam by using PU injection foam equipment .The foam formed has the characteristics as following:

1. The thermal conductivity is low, which can meets the requirements of city heating and energy saving.
2. Service life of the foam is very long, over 30 years.
3. High temperature resistance and good dimensional stability of the foam, the highest temperature range is 140 ºC.

TYPICAL PHYSICAL PROPERTIES

Physical Properities	Test Method	Metric	Value
Core Density	GB/T 6343-2009	kg/m^3	≥60
Radial Compressive Strength	GB/T 8813-2008	MPa	≥0.3
Initial Thermal Conductivity(50°C)	GB/T 10294-2008	W/(m·K)	≤0.033
Close Cell Content	GB/T 10799-2008	%	≥88
Water Absorption	GB/T 8810-2005	%	≤10
Air bubbles	GB/T 29047	mm	1/3Insulation thickness.
Average cell size.	GB/T 29047	mm	≤0.5

Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.

Other unmentioned matters and TDS&MSDS.Please visit our official website shundapu.en.made-in-china.com