Polyether Polyol Mattress Foam Pop 45% Foam

• Material: Polyurethanes/PU
• Usage: Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Blow Molding
• Color: White
• Hydroxyl Value: 380
• Acid Value: 0.15
• Water: 0.15
• Transport Package: 200kg/Drum
• Specification: Two components
• Trademark: Shunda
• Origin: China
• HS Code: 39072090
• Production Capacity: 50000ton/Year

Product Description

Technical Data Sheet

COPOLYMER POLYOL POP-2015

 

General Properties and Applications

POP-2015 is an inactive polyether polyol modified with a styrene-acrylonitrile (SAN) polymer with a solid content of approx 15% by weight. It can be used for the production of slabstock foams.


 

Data

 

Property	Value	Unit of measurement	Method
Hydroxyl number	45-49	mg KOH/g	GB/T12008.3-2009
Moisture	≤0.05	% by wt.	GB/T22313-2008
Viscosity 25ºC	800-1500	mPa.s	GB/T12008.7-2010
Solid conten	14-16	% by wt.	Q/0322SLH003-2017
Appearance	White to off-white	----------------------------	Visual

Handling Precautions

Flash point is above 200ºC (open cup method), flammable but non-explosive. In case of fire, put out with foams, dry powder, steam or water.
When handling polyols, avoid exposure to eyes or prolong contact with the skin. If eye contact occurs, flush with plenty of water. If skin contact occurs, wash exposed areas thoroughly with soap and water.

Storage

Recommended storage temperature (ºC):10-35

Shelf life (ex-works) 12 months if stored in sealed, moisture-tight containers.

Partially used containers should be tightly resealed due to the hygroscopic nature of the product. Recommended temperature for processing (ºC):20-25.