Polymeric Polyol Resin and Polymeric Mdi ISO for Rigid Spray Foam Insulation

• Customization: Available
• Material: Polyurethanes/PU
• Usage: General Plastics, Engineering Plastics
• Model NO.: SDP1337
• Plastic Properties After Heated: Thermosetting Plastic
• Plastic Forming Method: Reaction Injection Plastic
• Color: Yellow
• Cream Time: 0-2s
• Gel Time: 2-4s
• Tack Free Time: 5-7s
• Compressive Strength: ≥200kpa
• Application: Building
• Transport Package: 220kg/Drum
• Specification: Two components
• Trademark: shunda
• Origin: China
• HS Code: 39072090
• Production Capacity: 50000ton/Year
• Package Size: 60.00cm * 60.00cm * 90.00cm
• Package Gross Weight: 19.000kg

Product Description

SDP1337
BLEND POLYOL FOR BUILDING ROOF SPRAY

Product Description

SDP1337 is a kind of blend polyol used for rigid PU foam spray, specially used for the insulation of building roof. When it combined with isocyanate(PM200) leads to the formation of rigid polyurethane foam by using PU spray machine. The foam formed has the characteristics as following:

1. Zero ozone depleting blowing agent, Low global warming potential
2. The strong adhesive force, convenient construction and no seams.
3. The low thermal conductivity, low water absorption and good dimensional stability.

Product Parameters

Physical Properities		Standard	Unit	Value
Apparent Core density		GB/T 6343-2009	kg/m^3	48
Compressive strength		GB/T 8813-2008	kPa	≥200
Tensile strength		GB/T 9641-88	kPa	≥200
Closed cells		GB/T 10799-2008	%	≥90
Water absorption		GB/T 8810-2005	%	≤3
Surface Burning Characteristics (Flame spread Rating)		CAN/ULC-S102		<500
Initial thermal conductivity		GB/T 10294-2008	W/(m•K)	≤0.023
Dimensional stability (After 6days)	-25ºC	GB/T 8811-2008	%	≤±-1
	80ºC			≤±-1

Importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.

Usage Attentions

1. The thickness of one pass spray foam should not exceed 50 mm. If over 50mm, which may cause foam spontaneous combustion and poor foam performance.
2. It is suggested that spray next layer of the foam after the internal temperature of last spray foam blow 25ºC. And the maximum thickness spray during 24h period is 203mm(8inches).
3. Like most of foam product, foam made by SDP1337 is combustible. An thermal barrier must be installed in accordance with approved construction standards.
4. The service temperature of the foam with SDP1337 is between -60~80ºC.
5. The storage temperature of the blend polyol SDP1337 recommended 10-25ºC.

Other unmentioned matters and TDS&MSDS.